Plastics Technology - Dedicated to improving Plastics Processing.
Issue link: http://pty.epubxp.com/i/918111
So much for the why. What about the how? A hot-air dryer is recom- mended for drying polyolefins at tempera- tures in the range of 150 F to 180 F; a drying hopper should be sized for 2 hr of drying time. This type drying system will provide a stable incoming material temperature and lower the surface moisture of the pellets. The principle of operation of a hot-air dryer is simple: Hot air will absorb and hold more water than cool air; for example, ambient air at 75 F with a dewpoint temperature of 60 F has a relative humidity of 59.62%, meaning it has absorbed over half of the water that it can absorb at that temperature. If that air is then heated to a temperature above 75 F, as shown in Fig.1, the relative humidity of the air will decrease, and the drying air then will be able to absorb more water. A hot-air dryer will dry polyolefins down to 0.1% moisture, and often much lower, which will satisfy the vast majority of polyolefin processors. However, if your application requires an extraordinary low final moisture level, a dehumidifying dryer may be required. A dehumidifying dryer is a hot-air dryer on steroids. It first passes the drying air through a bed of molecular-sieve desiccant, which removes water from the drying air and lowers the air's dewpoint. The dehumidified air is then heated, which lowers the air's relative humidity. We now have drying air that has a very low dewpoint and an extremely low relative humidity (Fig. 2). A dehumidifying dryer can easily reduce the surface moisture of polyolefin pellets to 0.005% or lower. Note: Relative humidity is not a term used to describe the performance of dehumidifying dryers. It is used in this article to provide a reference when comparing the performance of a dehu- midifying dryer to that of a hot-air dryer. ABOUT THE AUTHOR: Pete Stoughton has more than 40 years' experi- ence with dehumidifying dryers and PET crystalizing systems. He has held various technical positions with the Conair Group, including tech- nical services manager, product manager, and business unit manager. He now has his own consulting firm, Polymer Drying Services. Contact: (814) 516-3838; pstoughton@comcast.net; pstoughton.com. any visible issues in most general-purpose molding and extrusion applications, increasing surface moisture levels will cause surface finish problems such as roughness, splay, or silver streaks. • Moving containers of polyolefins from an unheated warehouse into a warm and more humid production area may cause moisture to condense onto the cold pellets when the containers are opened. • Polyolefins that contain colorant such as carbon black, or are filled or reinforced, will attract and hold some surface moisture. • A good, high-quality surface finish is a necessity when plating polyolefin products, and even a very small amount of surface moisture present on the incoming pellets will result in a poor finish. DRYING BENEFITS AND TIPS Processors that have made the commitment to dry polyolefins have seen several benefits. Maintaining a consistent temperature and moisture level in the incoming material throughout the year helps them achieve consis- tent performance of the extruder or injection molding machine. What's more, reducing surface moisture on the incoming material results in an improved surface finish. Plus, preheating the material will reduce the energy load required from the injection molding or extrusion machine to melt the polymer. QUESTIONS ABOUT DRYING? Visit the Drying Zone. Preheating the material will reduce the energy load required from the injection molding or extrusion machine to melt the polymer. In a dehumidifying dryer, drying air is passed through a bed of molecular-sieve desiccant. The dehumidified air is then heated to a higher temperature, which lowers the air's relative humidity. We now have drying air that has a very low dewpoint and an extremely low relative humidity A dehumidifying dryer can easily reduce the surface moisture of polyolefin pellets to 0.005% or lower. FIG 2 Relative Humidity/Drying Temperature Drying Air is -40 F Dew Point % Relative Humidity Drying Temperature, F 60% 50% 40% 30% 20% 10% 0% 75 95 115 135 155 17 5 195 6.48 3.41 1.89 1.09 0.66 0.26 Filter Dessicant -40 F Dew Point Heater Dehumidifying Drying System Closed-Loop Air Circuit Drying Temperature 150 F to 180 F +60 F Ambient Air Dew Point 0.41 @plastechmag 55 Plastics Technology D R Y I N G P O LY O L E F I N S